Modelling the influence of plasticity induced softening on the low cycle fatigue and crack propagation behaviour of a nickel-based superalloy
(2023)
Journal Article
Cyclic hysteresis loops generated during high-temperature, isothermal, low-cycle fatigue testing of the nickel-based superalloy RR1000 revealed a gradual decrease in elastic modulus of up to 25 % compared to the initial value in dependence of the acc... Read More about Modelling the influence of plasticity induced softening on the low cycle fatigue and crack propagation behaviour of a nickel-based superalloy.