Mixed ionic-electronic conduction in K1/2Bi1/2TiO3

Li, Linhao; Li, Ming; Reaney, Ian M.; Sinclair, Derek C.

Abstract

Recently, it has been reported that the Pb-free piezoelectric perovskite Na1/2Bi1/2TiO3 (NBT) can be compositionally tuned by close control of the A-site starting stoichiometry to exhibit high levels of oxide-ion conduction. The related K1/2Bi1/2TiO3 (KBT) perovskite has also drawn considerable interest as a promising Pb-free piezoelectric material; however, its conduction properties have been less extensively investigated. Here we report on the influence of the K/Bi ratio in the starting composition on the electrical properties using a combination of impedance spectroscopy and ion-transport property measurements. KBT ceramics exhibit mixed ionic-electronic (oxide-ion) conduction with tion similar 0.5 at 600-800 degreeC and although variations in the A-site starting stoichiometry can create a similar1 order of magnitude difference in the bulk conductivity at >500 degree C, the conductivity is low (ca. 0.1 to 1 mS cm-1 at 700 degree C) and the activation energy for bulk conduction remains in the range similar1.2 to 1.5 eV. The high temperature electrical transport properties of KBT are therefore much less sensitive to the starting A-site stoichiometry as compared to NBT. However, KBT ceramics exhibit non-negligible proton conduction at lower temperatures (

Citation

Li, L., Li, M., Reaney, I. M., & Sinclair, D. C. (2017). Mixed ionic-electronic conduction in K1/2Bi1/2TiO3. Journal of Materials Chemistry C, 5(25), https://doi.org/10.1039/C7TC01786C

• Journal Article Type: Article
• Acceptance Date: Jun 1, 2017
• Online Publication Date: Jun 5, 2017
• Publication Date: Jul 7, 2017
• Deposit Date: Mar 1, 2018
• Publicly Available Date: Mar 1, 2018
• Journal: Journal of Materials Chemistry C
• Print ISSN: 2050-7526
• Electronic ISSN: 2050-7526
• Publisher: Royal Society of Chemistry
• Peer Reviewed: Peer Reviewed
• Volume: 5
• Issue: 25
• DOI: https://doi.org/10.1039/C7TC01786C
• Public URL: https://nottingham-repository.worktribe.com/output/871555
• Publisher URL: http://pubs.rsc.org/en/Content/ArticleLanding/2017/TC/C7TC01786C#!divAbstract
• Related Public URLs: http://pubs.rsc.org/en/content/articlehtml/2017/tc/c7tc01786c