Effect of test conditions on the temperature at which a protective debris bed is formed in fretting of a high strength steel

Hayes, E.K.; Shipway, P.H.

Abstract

It is well known that mechanisms and rates of fretting wear of many metals are dependent upon the temperature of the environment; specifically, it is known that a transition temperature exists, above which the debris forms a protective bed in the contact which results in very low rates of wear being observed. This paper seeks to investigate the influence of contact geometry and slip amplitude on the transition temperature of a high strength alloy steel, and to understand these effects in terms of debris retention in (or expulsion from) the contact. Cylinder-on-flat fretting tests were performed at temperatures between 25 °C and 250 °C with two displacement amplitudes (25 μm and 100 μm) and two cylinder radii (6 mm and 160 mm). It was found that for the smaller cylinder radius, the transition temperature increased as the fretting displacement amplitude was increased. However, it was found that whilst the contacts with 6 mm radius cylinders and 160 mm radius cylinders exhibited very different mechanisms of wear at low temperature, the temperature at which the transition to forming of the protective debris bed was not strongly influenced by the contact geometry; moreover, at the higher temperature, the protective bed is formed irrespective of contact geometry. It is proposed that the reduction in wear rate at higher temperatures is associated with the retention of oxide debris within in the contact area for long enough that it sinters to form a protective ‘glaze’ layer. By increasing the displacement amplitude, the rate at which the oxide is ejected from the fretting contact increases and this reduces the ability to form a protective layer; as such, a higher temperature is required to form the protective glaze as the displacement amplitude is increased.

Citation

Hayes, E., & Shipway, P. (2017). Effect of test conditions on the temperature at which a protective debris bed is formed in fretting of a high strength steel. Wear, 376-377(B), https://doi.org/10.1016/j.wear.2017.01.057

• Journal Article Type: Article
• Acceptance Date: Jan 13, 2017
• Online Publication Date: Jun 15, 2017
• Publication Date: Apr 15, 2017
• Deposit Date: Jun 16, 2017
• Publicly Available Date: Jun 16, 2017
• Journal: Wear
• Print ISSN: 0043-1648
• Electronic ISSN: 1873-2577
• Publisher: Elsevier
• Peer Reviewed: Peer Reviewed
• Volume: 376-377
• Issue: B
• DOI: https://doi.org/10.1016/j.wear.2017.01.057
• Keywords: Debris; Glaze; Temperature; Contact geometry
• Public URL: https://nottingham-repository.worktribe.com/output/856142
• Publisher URL: http://www.sciencedirect.com/science/article/pii/S0043164817301710
• Contract Date: Jun 16, 2017